• Silicone AFM / Hardener AFM

    Article No. 073780

    Silicone AFM / Hardener AFM

    Pourable, two-component silicone casting compound that cures at room temperature

    Variant
    Size / Quantity

    Note: This container size is being phased out and is only available to a limited extent.

    Product specifications

    Component A

    Density (20°C) 1.22 g/cm³
    Viscosity (20 °C) 25,000 mPas

    Component B

    Density (20°C) 1.04 g/cm³
    Viscosity (20 °C) 20 mPas

    Mixture

    Viscosity (20 °C) 24,000 mPas

    Once fully cured

    Linear shrinkage (7 days) approx. 0.5%
    Elongation at break (DIN 53504 S3A) approx. 380%
    Resistance to tear propagation (ASTM D 624 Form B) approx. 22 N/mm²
    Tensile strength (DIN 53504 S3A) approx. 2.8 N/mm²
    Shore A (DIN EN ISO 868) approx. 23

    The stated values represent typical product characteristics and are not to be construed as binding product specifications.

    Field of application

    • For use indoors and outdoors
    • Casting of high-value original pieces with accurate detail
    • Production of solid and main moulds
    • Forming with strong undercuts

    Properties

    • High reproduction accuracy and detail reproduction
    • Excellent resilience
    • Very good elasticity and tear resistance
    • Good flow properties
    • Easy demoulding
    • Preparation
      • Substrate requirements

        The substrate must be clean, dust-free and dry.

    • Application
      • Application temperature: min. 5 °C max. 30 °C
      • Drying time: can be worked over after 20 h
      • Application requirements

        Temperature of the material, air and substrate: from min. +5 °C to max. +30 °C

      • Pour or apply by brush

        Reaction time approx. 20 hours

    • Application instructions
      • The addition of up to 1% by mass of Thickening Additive AFM (0738) can increase the viscosity until stability is reached.

        To ensure that the vulcanised material is completely free of bubbles, degas the silicone/hardener mixture in a vacuum prior to use (max. 5 minutes at 10-20 mbar).

        Pourable resins, such as polyesters and polyurethanes, limit the ability to take a large number of impressions due to their aggressive nature.

        When making impression of critical substrates, e.g. materials that are porous, silicate-based or moisture-absorbing, use a silicone-free releasing agent (e.g. wallpaper paste).

        When creating supporting moulds, a suitable release agent must be applied to the outer skin of the silicone mould, e.g. Framework Paste (1121).

    • Working tools / cleaning
      • Paintbrush, spatula, stirrer

      • Clean tools immediately after use with thinner and brush cleaner.

        Pull off any cured residue.

    • Storage / shelf life
      • Store frost-free and cool / protect for moisture / close containers
      • Shelf-life 12 months
      • If stored unopened in its original container in a cool, dry place and protected against frost, the product will keep for at least 12 months.

    • Usage
      • 1.2 kg / l void
      • Approx. 1.2 kg/m²/mm layer thickness

    • General information
      • Current regulations and legal requirements must be taken into account and deviations from these must be agreed separately.

        The relevant test certificates must be observed when planning and carrying out work.

    • Disposal instructions
      • Larger quantities of leftover product should be disposed of in the original containers in accordance with the applicable regulations. Completely empty, clean containers should be recycled. Do not dispose of together with household waste. Do not allow to enter the sewage system. Do not empty into drains.

    • Safety / regulations
      • For further information on the safety aspects of transporting, storing and handling the product and on disposal and environmental matters, please see the current Safety Data Sheet.

    Possible system products